|
主题：钢制高频焊翅片管散热器生产工艺流程 [收藏主题] |
 Steel high frequency welding finned tube radiator production process: 1, material: steel pipe thickness is 2.5mm. High strength, good elongation 2, no crack after stamping, increase the corrosion resistance of the material itself. The oxidation corrosion of the steel is reduced, and the life of the radiator is ensured from the material. 2. Welding mode: Our company adopts fully automatic argon arc welding technology, one-sided welding, two-sided forming, uniform and smooth welding seam, no slag inclusion, no welding distillation, high welding quality, superior to other manufacturer's manual welding or resistance welding caused by welding defects. 3、防腐工艺：我公司增加了涂装内防腐工艺，可极大地增加散热器的寿命。防腐液选用国内先进的防腐涂料,防腐性能卓越。采用先进的真空防腐灌装，消除了散热器内腔尖角、焊渣处形成的死角气泡。 3. Anticorrosive process: our company has increased the anticorrosion process in the coating process, which can greatly increase the life of the radiator. The anticorrosive liquid selects the domestic advanced anticorrosive coating, the anticorrosive performance is outstanding. The advanced vacuum anti-corrosion filling eliminates the dead-angle bubbles formed at the sharp corner of the radiator chamber and the welding slag. 生产工艺流程：片头采购——焊接——打磨——切断（立柱钢管采购—切断）——对接点焊——焊接——打磨——单片试压——组装焊接——试压——前处理——内防腐涂装——烘干——喷涂——包装——成品 Production process: chip head purchasing - Welding - grinding - cutting (column steel pipe purchasing - cutting) - Butt spot welding - Welding - grinding - Monolithic pressure testing - assembling welding - pressure testing - Pretreatment - internal anti-corrosion coating - drying - spraying - Packaging - finished products ?钢制高频焊翅片管散热器生产工艺流程 Production process of steel high frequency welding finned tube radiator 4 翅片管焊接：采用高频自动焊接设备焊接，翅带焊接率≥85%。 4 finned tube welding: welding with high frequency automatic welding equipment. The welding rate of the wing belt is more than 85%. 5钢管分割：采用高速钢管锯分割，尺寸误差较小，以保证焊缝均匀。 5 steel pipe segmentation: using high-speed steel tube saws segmentation, small size error, to ensure uniform weld. 6封头冲压：采用专用设备一次冲压成型。 6 head stamping: special equipment is used for stamping forming at one time. 7连接件冲压：120T冲压成型。 7 connection stamping: 120T stamping. 8组片焊接：采用交流电焊接。 8 pieces of welding: alternating current welding. 9面罩冲压：采用120T冲压床及200T油压机压制完成。 9 mask stamping: press with 120T press bed and 200T oil press. 10面罩焊接：采用二氧化碳保护点焊接点焊。 10 mask welding: carbon dioxide protection spot welding. 11整：修整组片毛刺及缺陷，使组片光滑、平整。 11 integer: trimming the burrs and defects, make the pieces smooth and smooth. 12水压试验：试验压力为工作压力的1.5倍。 12 water pressure test: the test pressure is 1.5 times the working pressure. 13水压试验：试验压力为工作压力的1.5倍。 13 water pressure test: the test pressure is 1.5 times the working pressure. 14面罩前期处理：脱脂、水洗、碱蚀、水洗、出光、水洗、氧化磷化、水洗、烘干。 Pre-treatment of mask: degreasing, washing, alkali corrosion, washing, lighting, washing, phosphating, washing and drying. 15外表处理：采用高压喷沙工艺除去外表油污、锈迹。 15 surface treatment: high pressure sandblasting is used to remove exterior oil stains and rust. 16喷塑：采用优质环氧树脂涂料（环保），高压静电喷涂，高温180℃20min烘烤。 16 spraying: using high-quality epoxy resin coating (environmental protection), high-voltage electrostatic spraying, baking at high temperature 180 C for 20 minutes. 17内芯浸漆:将内芯整体浸泡在油漆中，保证各个部位均匀。 17 inner core dipping: immerse the inner core in the paint to ensure uniform parts. 18检验：成品检验 18 inspection: finished product inspection 19面罩包装：采用气垫膜包装。 19 mask packaging: air cushion film packaging. 辛苦整理.转载请注明http://www.wxsxsjx.com |
|
| 分享到 | |
 支持(0) |  反对(0)
 顶端  底部
|
![电子邮件:[ kesioncms@hotmail.com ]](http://www.510bj.com/club/images/email.gif){kind=small}
| ＜上一主题 | 下一主题 ＞ |